盾构隧道快硬高性能同步注浆材料研究

徐建平; 林文书; 许可; 林建平; 王彪; 苗强; 丁庆军

doi:10.3973/j.issn.1672-741X.2014.02.001

隧道建设 >

2014 , Vol. 34 >Issue 2: 95 - 100

DOI: https://doi.org/10.3973/j.issn.1672-741X.2014.02.001

研究与探索

盾构隧道快硬高性能同步注浆材料研究

徐建平 ,
林文书 ,
许可 ,
林建平 ,
王彪 ,
苗强 ,
丁庆军

展开

（1.武汉地铁集团有限公司, 湖北武汉 430030； 2.中铁一局集团有限公司, 陕西西安 710054； 3.武汉理工大学, 湖北武汉 430070）

徐建平（1971—），男，湖北恩施人，2006年毕业于武汉理工大学，材料学专业，博士，教授级高级工程师，主要从事隧道工程的建设工作。

收稿日期: 2013-07-19

修回日期: 2013-12-20

网络出版日期: 2014-02-27

收起

Study on Rapidhardening Highperformance Simultaneous  Grouting Material for Shieldbored Tunnels

XU Jianping ,
LIN Wenshu ,
XU Ke ,
LIN Jianping ,
WANG Biao ,
MIAO Qiang ,
Ding Qingjun

Expand

(1. Wuhan Metro Group Co., Ltd., Wuhan 430030, Hubei, China; 2. China Railway First Group Co., Ltd., Xi’an 710054, Shaanxi, China; 3.Wuhan University of Technology, Wuhan 430070, Hubei, China)

Received date: 2013-07-19

Revised date: 2013-12-20

Online published: 2014-02-27

Fold

摘要

为满足某些特殊盾构工况（地下水流大、断面水压高、冲刷力强）注浆工程及抢修、补注工程的顺利施工，需研制具有快硬、抗水分散性和稳定性好等特点的高性能同步注浆材料。以42.5快硬硫铝酸盐水泥(R.SAC42.5)、粉煤灰(FA)、矿渣微粉(SL)和砂作为基体材料，采用聚羧酸减水剂(PC)-膨润土(BE)-三乙醇胺早强剂(TEA)的复合保水、稳定、早强外加组分，优选配合比为R.SAC42.5∶FA∶SL∶BE∶砂∶水∶PC∶TEA=1∶3∶1∶0.5∶10∶2.25∶0.03∶0.08%，制备出初始流动度为210 mm、泌水率为014%、浆液pH值为9.6、1 d抗压强度为2.5 MPa的盾构隧道快硬高性能同步注浆材料。

关键词： 盾构隧道; 同步注浆; 快硬硫铝酸盐水泥; 膨润土; 早强剂

本文引用格式

徐建平 , 林文书 , 许可 , 林建平 , 王彪 , 苗强 , 丁庆军 . 盾构隧道快硬高性能同步注浆材料研究[J]. 隧道建设, 2014 , 34(2) : 95 -100 . DOI: 10.3973/j.issn.1672-741X.2014.02.001

Abstract

performance simultaneous grouting material with properties including rapid hardening, antwaterdispersion and good stability is needed in order to meet the requirements of the simultaneous grouting in shield tunneling under large water flow conditions, high water pressure conditions and high water flushing conditions. Rapidhardening highperformance simultaneous grouting material with 210 mm initial fluidity, 0.14% water bleeding rate, 9.6 pH value, and 2.5 MPa 1day compressive strength is obtained, with 42.5 rapid hardening sulphoaluminate cement (R. SAC42.5), fly ash(FA), slag(SL) and sand used as the main matrix materials, and waterreducing admixture(PC)bentonite(BE)triethanolamine accelerator(TEA) used as the water retaining, stable, and early strength additive components. The optimum mix of the rapidhardening highperformance simultaneous grouting material is that: R.SAC42.5∶FA∶SL∶BE∶sand∶water∶PC∶TEA=1∶3∶1∶0.5∶10∶2.25∶0.03∶0.08%. 

Key words： shieldbored tunnel; simultaneous grouting; rapid hardening sulphoaluminate cement; bentonite; rapid hardening agent

Options

文章导航

〈

〉

模态框（Modal）标题

摘要

本文引用格式

Abstract