适用于隧道混凝土裂缝修补的水性环氧树脂改性砂浆性能研究

doi:10.3973.j/issn.1672-741X.2016.04.005

隧道建设（中英文） ›› 2016, Vol. 36 ›› Issue (4): 398-402.DOI: 10.3973.j/issn.1672-741X.2016.04.005

适用于隧道混凝土裂缝修补的水性环氧树脂改性砂浆性能研究

鞠向伟¹，彭海龙²，高培伟^1,*，姚应征³，马爱群¹，张骏¹

（1. 南京航空航天大学土木工程系，江苏南京 210016； 2. 山西省交通规划勘察设计院，山西太原 030012； 3. 无锡地铁集团有限公司，江苏无锡 214000）

收稿日期:2015-06-29 修回日期:2016-01-20 出版日期:2016-04-20 发布日期:2016-04-27
作者简介:鞠向伟（1990—），男，辽宁凌源人，南京航空航天大学在读硕士，主要研究方向为混凝土材料。Email： 939324646@qq.com。*通讯作者：高培伟，Email： 1152976931@qq.com。
基金资助:
江苏省建设厅项目（2013ZD12）；江苏省六大人才项目（JZ-010）；无锡地铁项目（JS-201400361001）

Study of Properties of Modified Aqueous Epoxy Mortar Used in Rehabilitation of Tunnel Concrete Cracks

JU Xiangwei¹, PENG Hailong², GAO Peiwei^1，*, YAO Yingzheng³, MA Aiqun¹, ZHANG Jun¹

(1. Department of Civil Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, Jiangsu, China; 2. Shanxi Provincial Transportation Planning, Survey and Design Institute, Taiyuan 030012, Shanxi, China; 3. Wuxi Metro Group Co., Ltd., Wuxi 214000, Jiangsu, China)

Received:2015-06-29 Revised:2016-01-20 Online:2016-04-20 Published:2016-04-27

摘要/Abstract

摘要：

为提供一种可用于隧道管片破损及裂缝修补的高效修补材料，研发一种高强、高黏结性的水性环氧树脂改性水泥砂浆，研究改性砂浆抗折强度、抗压强度和黏结强度，并采用SEM等方法进行微观结构分析。试验结果表明： 1）随聚灰比增大，抗折强度和抗压强度先增大后减小； 2）在研究范围内，黏结强度随聚灰比的增加而减小； 3）改性后砂浆黏结强度增大20%~40%。

关键词: 管片修补, 改性砂浆, 黏结强度, 微观分析, 隧道裂缝

Abstract:

A kind of modified aqueous epoxy mortar with high performance and high bond strength for rehabilitation of tunnel segment cracks is developed. The properties of the mortar, including flexural strength, compressive strength and bond strength, are studied; then the microstructure of the mortar is analyzed by means of scanning electron microscope (SEM) method. The testing results show that: 1) The flexural strength and compressive strength increase with the polymercement ratio increases; and then they decrease at a peak. 2) The bond strength decreases with the polymercement ratio increases. 3) Compared to the traditional mortar, the bond strength of modified mortar increases by 20%-40%.

Key words: segment rehabilitation, modified mortar, bond strength, microcosmic analysis, tunnel crack

中图分类号:

U 45

鞠向伟，彭海龙，高培伟，姚应征，马爱群，张骏. 适用于隧道混凝土裂缝修补的水性环氧树脂改性砂浆性能研究[J]. 隧道建设, 2016, 36(4): 398-402.

JU Xiangwei, PENG Hailong, GAO Peiwei, YAO Yingzheng, MA Aiqun, ZHANG Jun. Study of Properties of Modified Aqueous Epoxy Mortar Used in Rehabilitation of Tunnel Concrete Cracks[J]. Tunnel Construction, 2016, 36(4): 398-402.

[1]	吴华明，张建纲，于诚，陆海梅. 水泥特性对低碱液体速凝剂的适应性影响[J]. 隧道建设, 2016, 36(5): 537-543.
[2]	邵义琴, 叶雅图, 史海欧, 王建. 隧道修复方案中结构安全性的有限元分析方法[J]. 隧道建设, 2011, 31(3): 325-329.

适用于隧道混凝土裂缝修补的水性环氧树脂改性砂浆性能研究

Study of Properties of Modified Aqueous Epoxy Mortar Used in Rehabilitation of Tunnel Concrete Cracks

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 2

编辑推荐

Metrics

本文评价