钢拱架锈蚀作用下型钢混凝土梁抗弯承载力研究

doi:10.3973/j.issn.2096-4498.2022.01.004

隧道建设（中英文） ›› 2022, Vol. 42 ›› Issue (1): 26-32.DOI: 10.3973/j.issn.2096-4498.2022.01.004

钢拱架锈蚀作用下型钢混凝土梁抗弯承载力研究

王明年^{1, 2}，刘轲瑞^{1, 2}，张艺腾^{1, 2}，杨恒洪^{1, 2}，于丽^{1, 2, *}

（1. 西南交通大学交通隧道工程教育部重点实验室，四川成都 610031； 2. 西南交通大学土木工程学院，四川成都 610031）

出版日期:2022-01-20 发布日期:2022-01-28
作者简介:王明年（1965—），男，安徽舒城人，1999年毕业于西南交通大学，桥梁与隧道工程专业，博士，教授，主要从事桥梁与隧道工程等领域的教学与科研工作。E-mail： 19910622@163.com。 *通信作者：于丽， E-mail： yuli_1026@home.swjtu.edu.cn。
基金资助:
国家自然科学基金（51878567,51878568）

Research on Flexural Capacity of Steel Reinforced Concrete Beams Subjected to Steel Arch Corrosion

WANG Mingnian^{1, 2}, LIU Kerui^{1, 2}, ZHANG Yiteng^{1, 2}, YANG Henghong^{1, 2}, YU Li^{1, 2,
*}

(1. Key Laboratory of Transportation Tunnel Engineering, Ministry of Education, Southwest Jiaotong University, Chengdu 610031, Sichuan, China; 2. School of Civil Engineering, Southwest Jiaotong University, Chengdu 610031, Sichuan, China)

Online:2022-01-20 Published:2022-01-28

摘要/Abstract

摘要： 针对海底隧道中的钢拱架锈蚀使初期支护承载力降低的问题,为从宏观角度体现锈蚀对于钢拱架承载力的影响,采用电加速腐蚀试验得到不同锈蚀率的钢拱架,并将不同锈蚀率的钢拱架混凝土梁进行抗弯承载力试验。结合数值模拟分析,得到以下结论: 1)锈蚀后的工字钢混凝土梁承载力随锈蚀率增加而减小,锈蚀率每增高1%，承载力平均下降 5.1 kN; 2)锈蚀工字钢混凝土梁加载过程中,当锈蚀率小于或等于1.5%时混凝土梁主要出现横向裂缝,锈蚀率大于1.5%时则主要出现贯通的纵向裂缝; 3)随着锈蚀率的增大,混凝土与工字钢之间的黏结作用减弱,混凝土应力、应变增大,反之工字钢应力、应变减小。

关键词: 海底隧道, 钢拱架锈蚀, 抗弯承载力, 抗弯承载力试验, 数值模拟

Abstract: Corrosion of the steel arch in the primary support in subsea tunnel reduces the primary support′s flexural capacity. Electrically accelerated corrosion tests obtain steel arches with different corrosion rates. Concrete beams of steel arches with different corrosion rates are tested to reflect the influence of corrosion on the flexural capacity of steel arches from a macroscopic point of view. The numerical simulation analysis results show the following: (1) The flexural capacity of corroded Isteel concrete beams decreases with increased corrosion rate. The average flexural capacity decreases by 5.1 kN as the corrosion rate increases by 1%. (2) Transverse cracks appear during the loading process of the corroded Ishaped steelconcrete beam when the corrosion rate is less than or equal to 1.5%, and longitudinal penetrated cracks appear when the corrosion rate is greater than 1.5%. (3) As the corrosion rate increases, the bonding effect between concrete and Ishaped steel weakens, and concrete stress and strain increase. On the contrary, the stress and strain of Ishaped steel decrease.

Key words: subsea tunnel, steel arch corrosion, flexural capacity, flexural capacity test, numerical simulation

中图分类号:

U 45

王明年, 刘轲瑞, 张艺腾, 杨恒洪, 于丽. 钢拱架锈蚀作用下型钢混凝土梁抗弯承载力研究[J]. 隧道建设, 2022, 42(1): 26-32.

WANG Mingnian, LIU Kerui, ZHANG Yiteng, YANG Henghong, YU Li. Research on Flexural Capacity of Steel Reinforced Concrete Beams Subjected to Steel Arch Corrosion[J]. Tunnel Construction, 2022, 42(1): 26-32.

[1]	吉艳雷, 陈刚. 铁路盾构隧道下穿新、旧高速公路桥桩保护技术研究——以广佛城际下穿佛开高速桥桩工程为例 [J]. 隧道建设, 2021, 41(S1): 288-.
[2]	吴忠仕, 贺祖浩, 刘文, 许超, 孔茜. 大直径泥水盾构始发钢套筒的防扭施工技术——以孟加拉卡纳普里河水下隧道为例[J]. 隧道建设, 2020, 40(S1): 321-326.

钢拱架锈蚀作用下型钢混凝土梁抗弯承载力研究

Research on Flexural Capacity of Steel Reinforced Concrete Beams Subjected to Steel Arch Corrosion

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 2

编辑推荐

Metrics

本文评价