临海环境对衬砌混凝土结构自防水性能影响研究

doi:10.3973/j.issn.2096-4498.2018.S2.014

隧道建设（中英文） ›› 2018, Vol. 38 ›› Issue (S2): 98-103.DOI: 10.3973/j.issn.2096-4498.2018.S2.014

临海环境对衬砌混凝土结构自防水性能影响研究

任辉¹，周先平¹，谭忠盛²，刘强²

（1. 港珠澳大桥珠海连接线管理中心，广东珠海 519030； 2. 北京交通大学土木建筑工程学院，北京 100044)

收稿日期:2018-06-26 修回日期:2018-08-09 出版日期:2018-12-30 发布日期:2019-01-30
作者简介:任辉（1986—），男，湖南常德人，2015年毕业于同济大学，隧道及地下建筑工程专业，硕士，工程师，主要从事软土隧道建设与研究工作。Email： ren445@126.com。
基金资助:
交通运输部建设科技项目（2013318J11300）

Study of the Influence of Coastal Environment on Selfwaterproof  Performance of Lining Concrete Structures

REN Hui¹, ZHOU Xianping¹, TAN Zhongsheng², LIU Qiang²

(1. The Management Center of Zhuhai Link Road of Hong KongZhuhaiMacao Bridge, Zhuhai 519030,  Guangdong, China; 2. School of Civil Engineering, Beijing Jiaotong University, Beijing 100044, China)

Received:2018-06-26 Revised:2018-08-09 Online:2018-12-30 Published:2019-01-30

摘要/Abstract

摘要：

为获得合理的临海隧道衬砌混凝土配合比和提高混凝土自防水性能，以拱北隧道工程为背景，开展混凝土在临海侵蚀环境下的自防水性能试验研究。基于系统化的混凝土配合比设计方法确定防水混凝土初步配合比，通过碳化和硫酸盐侵蚀室内试验模拟临海环境对混凝土自防水性能的影响，对混凝土抗压强度、抗水渗透和抗氯离子渗透3个指标进行试验分析，最终获得最优配合比。结果表明： 1）复掺(20%粉煤灰+10%矿渣)混凝土自防水性能最好，该方案可作为拱北隧道主体结构混凝土配合比； 2）在碳化和硫酸盐侵蚀作用下，混凝土的抗氯离子渗透能力随时间逐渐减弱、抗压强度随时间逐渐增强； 3）混凝土掺合料对抗氯离子渗透能力的增强作用非常明显，但对混凝土后期强度增幅有一定的影响。

关键词: 临海隧道, 混凝土自防水, 混凝土配合比, 室内试验

Abstract:

In order to obtain reasonable mix ratio of coastal tunnel lining concrete and improve selfwaterproof performance of concrete，taking the Gongbei Tunnel project as background, the selfwaterproof performance study of concrete in the coastal erosion environment is carried out. The preliminary mix ratio of the waterproof concrete is determined based on systematic concrete mix ratio design method. The influence of the coastal environment on the selfwaterproofing performance of concrete is simulated by carbonation and sulfate erosion laboratory test. Through the test analysis of concrete compressive strength, water resistance and chloride ion resistance, the optimal mixture ratio is obtained. The result shows that: (1)The concrete with 20% fly ash and 10% slag has the best selfwaterproof performance, which can be used as the main structure of Gongbei Tunnel. (2)Under the carbonation and sulfate erosion, the chloride ion resistance of concrete decreases with time and its compressive strength increases. (3)The strengthening effect of concrete admixtures on chloride ion resistance is very obvious, but it has certain influence on the increase of concrete strength in later period.

Key words: coastal tunnel, selfwaterproofing of concrete, mix ratio of concrete, laboratory test

中图分类号:

U 459.5

任辉，周先平，谭忠盛，刘强. 临海环境对衬砌混凝土结构自防水性能影响研究[J]. 隧道建设, 2018, 38(S2): 98-103.

REN Hui, ZHOU Xianping, TAN Zhongsheng, LIU Qiang. Study of the Influence of Coastal Environment on Selfwaterproof  Performance of Lining Concrete Structures[J]. Tunnel Construction, 2018, 38(S2): 98-103.

[1]	许华国, 陈馈, 孙振川. 盾构刀盘切削钢筋混凝土桩基室内试验研究 [J]. 隧道建设, 2020, 40(1): 35-42.
[2]	吕乾乾，孙振川，杨振兴，陈瑞祥，张兵. 海水环境下盾构泥浆性能试验研究[J]. 隧道建设, 2019, 39(2): 211-218.
[3]	黄涛，刘泉声，黄兴，张晓平，路新景. 刮刀磨损实时监测系统研发及室内验证试验研究[J]. 隧道建设, 2018, 38(S2): 364-373.
[4]	王志杰，李瑞尧，徐海岩，唐力，徐君祥，周平. 蒙华铁路阳城隧道土砂分界地层分界面位置对围岩稳定性影响探究[J]. 隧道建设, 2018, 38(9): 1435-1445.
[5]	杨春山，魏立新，陈凌伟，汪传智. 高水位环境下沉管隧道模袋砂围堰破坏模式研究[J]. 隧道建设, 2018, 38(9): 1505-1512.
[6]	彭奇，刘国峰，杨腾，陈立. 强降雨条件下岩溶地质环境因素对隧道安全性的影响序列研究[J]. 隧道建设, 2018, 38(7): 1149-1157.
[7]	杨卓. 圆梁山隧道高压富水区衬砌混凝土理论配合比研究[J]. 隧道建设, 2005, 25(2): 10-12，17.

临海环境对衬砌混凝土结构自防水性能影响研究

Study of the Influence of Coastal Environment on Selfwaterproof  Performance of Lining Concrete Structures

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 7

编辑推荐

Metrics

本文评价